KAOLIN

Kaolin, or China clay is a part of Group of Minerals, which is nearly white in color. It is distinguished from other industrial clays based on its fine particle size and pure coloring. The primary constituent in kaolin is the mineral kaolinite. Kaolin has different grades for different applications.

Applications:

  • Ceramics / Tiles
  • Porcelain and Table ware
  • Sanitary ware
  • Refractories
  • Glazes and Engobes
  • Paper
  • Paint
  • Rubber

 

TECHNICAL DATA SHEET - KAOLIN (KN-83)

 

PHYSICAL PROPERTIES

Moisture                                                  16 %

Firing at 1200 °C

Specific Gravity                                       2.600 g/m3

Fired Colour Chromameter (L)              >97 %

Bulk Density                                            1.000 kg/m3

Fired Colour Blue Filter (457 nm)         >83 %

Modules of rapture                               10.5    Mpa

Shrinkage                                                   6.5 %

Refractoriness                                        1760 °C

Water Absorption                                     22 %

 

 CHEMICAL ANALYSIS

Al2O3                                       38.0 %

K2O                                                0.25 %

Sio2                                           46.5 %

NA2                                                0.03 %

Fe2o3                                       <0.3 %

Loss on ignition                           13.6 %

TiO2                                       <1.10 %       

 

 

MINERALALOGICAL COMPOSITION

Kaolinite                                                   95 %

Quartz                                                  3%

Muscovite                                                < 2%

Other                                                    1 %

 

PARTICLE SIZE ANALYSIS, LAZER

Residue at 40 μm

<0.5 %

Less than 20 μm

84 %

Less than 10 μm

70%

Less than 5   μm

55%

Less than 2   μm

33%

Less than 1   μm

18%

 

TECHNICAL DATA SHEET - KAOLIN (KC-1)

 

PHYSICAL PROPERTIES

Moisture                                                      16 %

Specific Gravity                             2.600 g/m3

Bulk Density                                 1.000 kg/m3

Modules of rapture                              25 Mpa

Refractoriness                                      1760 °C

Firing at 1200 °C

Fired Colour Chromameter (L)              95 %

Fired Colour Blue Filter (457 nm)         81 %

Shrinkage                                                     8 %

Water Absorption                                     20 %

 

 CHEMICAL ANALYSIS

Al2O3                                                   37.0 %

Sio2                                                       47.0 %

Fe2o3                                                   0.90 %

TiO2                                                      0.60 %

K2O                                                          0.35 %

NA2                                                      < 0.04 %

Fluorite                                           < 250 ppm

Loss on ignition                                    13.4 %

 

MINERALALOGICAL COMPOSITION

Kaolinite                                                      92 %

Other                                                             8%

 

PARTICLE SIZE ANALYSIS, SEDIGRAPH

Residue at 40μm                                                                                                                     <0.5 %

Less than 20 μm                                                                                                                         99 %

Less than 10 μm                                                                                                                         88 %

Less than 5   μm                                                                                                                          75 %

Less than 2   μm                                                                                                                         58 %

 

PARTICLE SIZE ANALYSIS, LAZER

D90                                                                                                                                                           20 μm

D50                                                                                                                                                           5 μm

D20                                                                                                                                                           1.5μm

D5                                                                                                                                                              0.6 μm